Electrical conductivity in Li2O2 and its role in determining capacity limitations in non-aqueous Li-O2 batteries

Publication: Research - peer-reviewJournal article – Annual report year: 2011

View graph of relations

Non-aqueous Li-air or Li-O2 cells show considerable promise as a very high energy density battery couple. Such cells, however, show sudden death at capacities far below their theoretical capacity and this, among other problems, limits their practicality. In this paper, we show that this sudden death arises from limited charge transport through the growing Li 2O2 film to the Li2O2-electrolyte interface, and this limitation defines a critical film thickness, above which it is not possible to support electrochemistry at the Li2O 2-electrolyte interface. We report both electrochemical experiments using a reversible internal redox couple and a first principles metal-insulator-metal charge transport model to probe the electrical conductivity through Li2O2 films produced during Li-O 2 discharge. Both experiment and theory show a sudden death in charge transport when film thickness is ∼5 to 10 nm. The theoretical model shows that this occurs when the tunneling current through the film can no longer support the electrochemical current. Thus, engineering charge transport through Li2O2 is a serious challenge if Li-O2 batteries are ever to reach their potential. © 2011 American Institute of Physics.
Original languageEnglish
JournalJournal of Chemical Physics
Publication date2011
Volume135
Issue21
Pages214704
ISSN0021-9606
DOIs
StatePublished

Bibliographical note

© 2011 American Institute of Physics.

CitationsWeb of Science® Times Cited: 67
Download as:
Download as PDF
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
Word

Download statistics

No data available

ID: 6377232