Effects of Zr Doping on Magnetic and Structural Properties of DyBa2Cu3O 7−δ Thin Films  

Publication: Research - peer-reviewJournal article – Annual report year: 2018

DOI

View graph of relations

DyBa2(Cu 1−x-Zrx )3 O 7−δ thin films (with x = 0.00, 0.02, 0.04, and 0.06) were synthetized using the chemical solution deposition method on single crystalline LaAlO3 substrates. Effects resulting from Zr doping were investigated by means of magnetic and structural measurements. X-ray diffraction analysis demonstrated a strong c-axis orientation in the DyBa 2(Cu1−x -Zrx) 3 O 7−δ thin films, with only minor reflections due to the presence of Dy2 O 3 and BaZrO3 phases. Narrow transitions with Δ Tc ranging from 1 to 2 K for samples with x = 0.00 and 0.06, respectively, were observed in ac magnetic susceptibility curves, where the nondoped sample demonstrated the highest T onsetc of 91.7 K compared to the Zr-doped samples. Critical current densities Jc of the thin films were obtained from magnetization loop measurements with applied magnetic fields up to 6 T and by employing the Bean model. The sampled doped with 4% Zr exhibited the highest J c value (J c = 3.5 MA/cm 2, self-field, 77 K) in the low field range and we, in general, observed that Zr-doped films demonstrated higher values compared to the pure sample. Pinning force plots ( Fp versus B ) reveal a significant improvement over the magnetic field range investigated of the maximum pinning force for Zr-doped samples. We found FMaxp = 1.7 GN/m3 and 3.8 GN/m 3 for pure and 6% Zr samples, respectively. Analysis based on the Dew-Hughes model shows that normal surface pinning is the dominating pinning mechanism.
Original languageEnglish
Article number8000804
JournalI E E E Transactions on Applied Superconductivity
Volume28
Issue number4
Number of pages4
ISSN1051-8223
DOIs
StatePublished - 2018
CitationsWeb of Science® Times Cited: 0

    Keywords

  • Superconducting, thin film, Zr-doping, critical current density
Download as:
Download as PDF
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
Word

ID: 147972073