Dynamic studies of catalysts for biofuel synthesis in an Environmental Transmission Electron Microscope

Publication: Research - peer-reviewConference abstract in proceedings – Annual report year: 2011

Documents

View graph of relations

The development of transportation fuels from sustainable resources requires new and better production paths. One approach involves the use of biogas to synthesize alcohols, such as methanol or higher alcohols for fuel. For the production of methanol a reduction of processing temperature and pressure to lower the process cost and make the product more competitive is desired. Higher alcohols are in general favourable over methanol due to their high energy density and ease of use in current internal combustion engines. However, the yield of higher alcohols in present production routes is poor prompting for the development of better catalysts [1]. The Catalysis for Sustainable Energy Project (CASE) at the Technical University of Denmark aims at discovering new and improved catalysts based on density functional theory and on testing the chemical reactivity of the most promising candidates experimentally. Transmission electron microscopy (TEM) is used for microstructural characterization and provides feedback for both theory and synthesis. TEM is a powerful tool for characterizing of catalysts. However, conventional TEM does not provide dynamic information about catalysts in their working state. We have recently installed an environmental transmission electron microscope (ETEM) equipped with a differential pumping system to confine a controlled flow of gas around the specimen, allowing observation in a gaseous environment (FEI Titan E-cell, monochromated, objective lens aberration corrector, Gatan imaging filter). In combination with a heating holder, this microscope allows catalysts to be studied using a variety of TEM techniques in situ in a reactive environment approaching the working conditions of the catalysts [2,3]. Here, we present recent ETEM studies of newly synthesized catalysts for alcohol synthesis. Using High-Resolution TEM, electron diffraction, energy electron-loss spectroscopy (EELS), Energy Dispersive X-ray spectroscopy (EDX) and High-Angle Annular Dark Field (HAADF) investigations we have studied the structural changes of these catalysts. Complementary obeservations have been done using Extended X-ray Absorption Fine Structure (EXAFS). The experimental findings have been correlated with the observed changes in the chemical activity of the catalysts. Systematic studies involving variation in temperature, gas pressure and composition were performed and related to structural changes in the specimen. Representative TEM images of a CuSn based catalyst for synthesis of higher alcohols are shown in Figure 1. The CuSn particles are observed to sinter during the reduction leading to a decreased activity of the catalyst. Figure 2 shows the distribution of Co and Mo in a Co/MoS2 catalyst during treatment in 1.5 mbar H2 at 600K. The Co phase is seen to segregate from MoS2. The EDX scans in Figure 2 b) and c) indicate this segregation.
Original languageEnglish
Title of host publicationMC 2011 Kiel : Microscopy Conference 2011
PublisherDGE – German Society for Electron Microscopy
Publication date2011
PagesM3-336
ISBN (print)978-3-00-033910-3
StatePublished

Conference

ConferenceMicroscopy Conference MC 2011
CountryGermany
CityKiel
Period28/08/1102/09/11
Internet addresshttp://www.mc2011.de/

Bibliographical note

Oral presentation.

Keywords

  • Biofuel, Environmental TEM, Catalysis
Download as:
Download as PDF
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
Word

Download statistics

No data available

ID: 6236024