Disorientations and work-hardening behaviour during severe plastic deformation

Publication: Research - peer-reviewConference article – Annual report year: 2012

View graph of relations

Orientation differences develop during plastic deformation even in grains of originally uniform orientation. The evolution of these disorientations is modelled by dislocation dynamics taking into account different storage mechanisms. The predicted average disorientation angles across different types of boundaries are in agreement with experimental data for small and moderate plastic strains. At large plastic strains after severe plastic deformation, saturation of the measured average disorientation angle is observed. This saturation is explained as an immediate consequence of the restriction of experimentally measured disorientation angles to angles below a certain maximum value imposed by crystalline symmetry. Taking into account the restrictions from crystalline symmetry for modelled disorientation angles does not only lead to an excellent agreement with experimental findings on Ni after high pressure torsion, but also rationalizes the work-hardening behaviour at large plastic strains as well as a saturation of the flow stress.
Original languageEnglish
JournalRisoe International Symposium on Materials Science. Proceedings
Volume33
Pages (from-to)331-336
ISSN0907-0079
StatePublished - 2012
Peer-reviewedYes

Conference

Conference33rd Risø International Symposium on Materials Science
CountryDenmark
CityRoskilde
Period03/09/201207/09/2012

Bibliographical note

Proceedings of the 33rd Risø International Symposium on Materials Science : Nanometals - Status and Perspective

Download as:
Download as PDF
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
Word

ID: 12696675