Direct observation of 3-D grain growth in Al–0.1% Mn

Publication: Research - peer-reviewJournal article – Annual report year: 2008

View graph of relations

Grain growth in an Al-0.1% Mn sample has been measured non-destructively using a three-dimensional X-ray diffraction (3DXRD) microscope. The 3-D grain morphology as well as the crystallographic orientation was determined for 483 grains in the illuminated volume prior to annealing. After annealing, a second map revealed that significant grain growth had taken place, with only 27 remaining grains in the same volume. The correlation between grain orientation, growth of grains and neighbouring relationships is explored. (c) 2008 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
Original languageEnglish
JournalScripta Materialia
Volume59
Issue number5
Pages (from-to)491-494
ISSN1359-6462
DOIs
StatePublished - 2008
Peer-reviewedYes
CitationsWeb of Science® Times Cited: 38
Download as:
Download as PDF
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
Word

ID: 3250752