Polymer electrolyte membrane (PEM) water electrolysis is a prospective method of producing hydrogen. We focused on one of its issues – the lack of a suitable support material for the anode electrocatalyst. TaC and NbC were studied as possible electrocatalyst supports for the PEM water electrolysis. Resistance to oxidation of the TaC and NbC was investigated by exposing them to air at 84 and 150 °C. Subsequently, their electrical conductivity was measured as the indicator of oxidation. Change in specific surface area and conductivity was measured after different periods of ball milling. We found that the TaC was significantly more resistant to oxidation than the NbC. Eventually, both materials retained relatively high electrical conductivity even with the oxidized surface. TaC can thus be recommended as an electrocatalyst support for the oxygen evolution reaction and both materials are proposed to be tested as alternative electrocatalyst supports for the hydrogen evolution reaction
Original languageEnglish
JournalE C S Transactions
Publication date2013
Volume45
Issue21
Pages59-67
ISSN1938-5862
StatePublished

Conference

Conference221th ECS meeting
CountryUnited States
CitySeattle, WA
Period06/05/1210/05/12
Download as:
Download as PDF
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
Word

ID: 51142841