Determining grain resolved stresses in polycrystalline materials using three-dimensional X-ray diffraction

Publication: Research - peer-reviewJournal article – Annual report year: 2010

View graph of relations

An algorithm is presented for characterization of the grain resolved (type II) stress states in a polycrystalline sample based on monochromatic X-ray diffraction data. The algorithm is a robust 12-parameter-per-grain fit of the centre-of-mass grain positions, orientations and stress tensors including error estimation and outlier rejection. The algorithm is validated by simulations and by two experiments on interstitial free steel. In the first experiment, using only a far-field detector and a rotation range of 2 × 110°, 96 grains in one layer were monitored during elastic loading and unloading. Very consistent results were obtained, with mean resolutions for each grain of approximately 10 µm in position, 0.05° in orientation, and 8, 20 and 13 × 10-5 in the axial, normal and shear components of the strain, respectively. The corresponding mean deviations in stress are 30, 50 and 15 MPa in the axial, normal and shear components, respectively, though some grains may have larger errors. In the second experiment, where a near-field detector was added, ~ 2000 grains were characterized with a positional accuracy of 3 µm.
Original languageEnglish
JournalJournal of Applied Crystallography
Publication date2010
Volume43
Issue3
Pages539-549
ISSN0021-8898
DOIs
StatePublished
CitationsWeb of Science® Times Cited: 33

Keywords

  • Materials characterization and modelling, Materials and energy storage
Download as:
Download as PDF
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
Word

ID: 4547719