Combined XRD and XANES studies of a Re-promoted Co/γ-Al2O3 catalyst at Fischer–Tropsch synthesis conditions

Publication: Research - peer-reviewJournal article – Annual report year: 2010

View graph of relations

A cobalt based Fischer–Tropsch catalyst was studied during the initial stages of the reaction at industrially relevant conditions. The catalyst consists of 20wt% cobalt supported on γ-Al2O3 and promoted by 1wt% of rhenium. X-ray diffraction (XRD) in combination with X-ray absorption near edge structure (XANES) were used to reveal information on the particle and crystallite size and the oxidation states of the active component. Conditions giving high selectivity towards light hydrocarbons (methanation, 673K, 10bar and high GHSV) were compared to conditions were higher hydrocarbons are the main products (FT synthesis at 483K, 18bar and low GHSV). The data analysis shows no significant changes in the cobalt crystallites during the first hours of Fischer–Tropsch synthesis. Running the reaction at higher temperatures and predominantly methanation conditions led to significant sintering of the cobalt particles and a further reduction of a partially reduced catalyst could be observed.
Original languageEnglish
JournalCatalysis Today
Publication date2010
Volume155
Issue3-4
Pages289-295
ISSN0920-5861
DOIs
StatePublished
CitationsWeb of Science® Times Cited: 26

Keywords

  • Batteries and carbon-free energy storage, Materials and energy storage
Download as:
Download as PDF
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
Word

ID: 5612041