title = "Characterization of Metalloproteins and Biomaterials by X-ray Absorption Spectroscopy and X-ray Diffraction",
publisher = "DTU Chemistry",
author = "Frankær, {Christian Grundahl} and Kenny Ståhl and Pernille Harris",
year = "2012",

}

RIS

TY - BOOK

T1 - Characterization of Metalloproteins and Biomaterials by X-ray Absorption Spectroscopy and X-ray Diffraction

A1 - Frankær,Christian Grundahl

AU - Frankær,Christian Grundahl

A2 - Ståhl,Kenny

A2 - Harris,Pernille

ED - Ståhl,Kenny

ED - Harris,Pernille

PB - DTU Chemistry

PY - 2012

Y1 - 2012

N2 - <p>This thesis presents thework on combining complementary X-rays techniques for studying the structures of proteins and other biomaterials, and consists of three different projects: (<em>i</em>) Characterization of protein powders with X-ray powder diffraction (XRPD). (<em>ii</em>) The combination of X-ray crystallography and X-ray absorption spectroscopy (XAS) applied to studying different hexameric insulin conformations. (<em>iii</em>) The structures of polymorphs of strontium ranelate and the distribution of strontium in bone tissue.<br/> A procedure for fast identification and verification of protein powders using XRPD was developed and tested on micro-crystals of lysozyme and insulin. Different protein crystal forms were identified by comparing experimental powder diffraction patternswith patterns calculated from PDB coordinates. The key factor to bring the calculated patterns in agreement with the observed patterns was correction for disordered bulk-solvent, but also correction for background and optimization of unit cell parameters have to be taken into account. A sample holder was designed for collecting powder diffraction data on a standard laboratory X-ray powder diffractometer. The background was reduced by use<br/> of pinholes integrated in the sample holder design, and crystal forms of well diffracting protein powders were safely identified from only 7 μl of sample. The sample holder was furthermore adaptable for XAS experiments.<br/> The crystal structures of three conformations of hexameric bovine zinc insulin (T<sub>6</sub>, T<sub>3</sub>R<sub>3</sub> and R<sub>6</sub>) were solved by single crystal X-ray diffraction (XRD) to 1.40 Å, 1.30 Å and 1.80 Å resolution, respectively. The zinc coordination in each conformation was studied by XAS including both extended X-ray absorption fine structure (EXAFS) spectroscopy and X-ray absorption near edge structure (XANES) spectroscopy. High quality XAS spectra were collected at the Zn K-edge on insulin micro-crystals with EXAFS signal up to 14 Å<sup>−1</sup> in <em>k</em>-space. Regarding the hexamer as a dimer of trimers where each trimer contains a Zn<sup>2</sup>+ ion, zinc adopted tetrahedral coordination in all R3-trimers, and octahedral coordination in T<sub>3</sub>-trimers. The coordination distances to zinc were refined from EXAFS with standard deviations below 0.01 Å for the first coordination sphere. In contrast to the distances determined from the medium resolution crystal structures, the XAS results were in good agreement with distances found in small molecules with similar coordination geometries, as well as in other high resolution insulin structures. As the radiation doses for the XRD experiments were significantly higher compared to that of XAS experiments, the single crystals were exposed to a higher degree of radiation damage affecting the zinc coordination in the T<sub>3</sub>-sites, in particular. Furthermore, XANES spectra for the zinc sites in T<sub>6</sub> and R<sub>6</sub> insulin were successfully calculated using finite difference methods, and the bond distances and angles were optimized from a quantitative XANES analysis.<br/> T<sub>6</sub> insulin was furthermore crystallized with iron, nickel and copper, and their XRD crystal structures were solved to 1.90 Å, 1.50 Å and 1.45 Å resolution, respectively. As the affinity to iron is low, iron insulin crystals were grown in presence of small amounts of zinc. The two metal sites in the XRD structure thus contained respectively one Fe<sup>2</sup>+ and one Zn<sup>2</sup>+ ion, with respectively tetrahedral and octahedral coordination geometry. The metal sites in nickel and copper insulin were studied by XAS. Coordination distances were refined from EXAFS showing a very regular octahedral coordination of Ni<sup>2</sup>+, which was further verified by calculated XANES spectra. The coordination geometry of copper<br/> was, however, ambiguously determined in the XRD structure of copper insulin. The XANES spectrum revealed the presence of copper in oxidation state +I, which was caused by photoreduction of Cu<sup>2</sup>+ during the XAS experiments. Photoreductionwas not observed for nickel and zinc insulin. EXAFS analysis showed a tetrahedral coordination of copper, which was further supported by ab initio Hartree-Fock calculations, as well as calculated XANES spectra.<br/> Strontium ranelate, a pharmaceutical used in the treatment of osteoporosis, was synthesized and crystallized and the crystal structure of the nonahydrate was solved. The crystalswere highly sensitive to humidity and temperature and easily deteriorate upon dehydration. Four other hydrates were observed by <em>in situ</em> XRPD upon dehydration. These were identified as heptahydrate, pentahydrate, trihydrate and dihydrate by estimation of the water content by thermogravimetric analysis. <br/> Bone tissue from dogs treated with strontiummalonate was studied using XAS. A new approach for analysing the X-ray absorption spectra resulted in a compositional model, from which the relative distribution of strontium in the different bone composites was estimated. Approximately 35–45 % of the strontium present was incorporated into calcium hydroxyapatite by substitution of some of the calcium ions, and at least 30 % was located at sites with a high structural disorder similar to Sr<sup>2</sup>+ in solution. The remaining strontium was absorbed in collagen. The relative distribution of strontium among the different composites seemed to be independent of treatment period and dose level.</p>

AB - <p>This thesis presents thework on combining complementary X-rays techniques for studying the structures of proteins and other biomaterials, and consists of three different projects: (<em>i</em>) Characterization of protein powders with X-ray powder diffraction (XRPD). (<em>ii</em>) The combination of X-ray crystallography and X-ray absorption spectroscopy (XAS) applied to studying different hexameric insulin conformations. (<em>iii</em>) The structures of polymorphs of strontium ranelate and the distribution of strontium in bone tissue.<br/> A procedure for fast identification and verification of protein powders using XRPD was developed and tested on micro-crystals of lysozyme and insulin. Different protein crystal forms were identified by comparing experimental powder diffraction patternswith patterns calculated from PDB coordinates. The key factor to bring the calculated patterns in agreement with the observed patterns was correction for disordered bulk-solvent, but also correction for background and optimization of unit cell parameters have to be taken into account. A sample holder was designed for collecting powder diffraction data on a standard laboratory X-ray powder diffractometer. The background was reduced by use<br/> of pinholes integrated in the sample holder design, and crystal forms of well diffracting protein powders were safely identified from only 7 μl of sample. The sample holder was furthermore adaptable for XAS experiments.<br/> The crystal structures of three conformations of hexameric bovine zinc insulin (T<sub>6</sub>, T<sub>3</sub>R<sub>3</sub> and R<sub>6</sub>) were solved by single crystal X-ray diffraction (XRD) to 1.40 Å, 1.30 Å and 1.80 Å resolution, respectively. The zinc coordination in each conformation was studied by XAS including both extended X-ray absorption fine structure (EXAFS) spectroscopy and X-ray absorption near edge structure (XANES) spectroscopy. High quality XAS spectra were collected at the Zn K-edge on insulin micro-crystals with EXAFS signal up to 14 Å<sup>−1</sup> in <em>k</em>-space. Regarding the hexamer as a dimer of trimers where each trimer contains a Zn<sup>2</sup>+ ion, zinc adopted tetrahedral coordination in all R3-trimers, and octahedral coordination in T<sub>3</sub>-trimers. The coordination distances to zinc were refined from EXAFS with standard deviations below 0.01 Å for the first coordination sphere. In contrast to the distances determined from the medium resolution crystal structures, the XAS results were in good agreement with distances found in small molecules with similar coordination geometries, as well as in other high resolution insulin structures. As the radiation doses for the XRD experiments were significantly higher compared to that of XAS experiments, the single crystals were exposed to a higher degree of radiation damage affecting the zinc coordination in the T<sub>3</sub>-sites, in particular. Furthermore, XANES spectra for the zinc sites in T<sub>6</sub> and R<sub>6</sub> insulin were successfully calculated using finite difference methods, and the bond distances and angles were optimized from a quantitative XANES analysis.<br/> T<sub>6</sub> insulin was furthermore crystallized with iron, nickel and copper, and their XRD crystal structures were solved to 1.90 Å, 1.50 Å and 1.45 Å resolution, respectively. As the affinity to iron is low, iron insulin crystals were grown in presence of small amounts of zinc. The two metal sites in the XRD structure thus contained respectively one Fe<sup>2</sup>+ and one Zn<sup>2</sup>+ ion, with respectively tetrahedral and octahedral coordination geometry. The metal sites in nickel and copper insulin were studied by XAS. Coordination distances were refined from EXAFS showing a very regular octahedral coordination of Ni<sup>2</sup>+, which was further verified by calculated XANES spectra. The coordination geometry of copper<br/> was, however, ambiguously determined in the XRD structure of copper insulin. The XANES spectrum revealed the presence of copper in oxidation state +I, which was caused by photoreduction of Cu<sup>2</sup>+ during the XAS experiments. Photoreductionwas not observed for nickel and zinc insulin. EXAFS analysis showed a tetrahedral coordination of copper, which was further supported by ab initio Hartree-Fock calculations, as well as calculated XANES spectra.<br/> Strontium ranelate, a pharmaceutical used in the treatment of osteoporosis, was synthesized and crystallized and the crystal structure of the nonahydrate was solved. The crystalswere highly sensitive to humidity and temperature and easily deteriorate upon dehydration. Four other hydrates were observed by <em>in situ</em> XRPD upon dehydration. These were identified as heptahydrate, pentahydrate, trihydrate and dihydrate by estimation of the water content by thermogravimetric analysis. <br/> Bone tissue from dogs treated with strontiummalonate was studied using XAS. A new approach for analysing the X-ray absorption spectra resulted in a compositional model, from which the relative distribution of strontium in the different bone composites was estimated. Approximately 35–45 % of the strontium present was incorporated into calcium hydroxyapatite by substitution of some of the calcium ions, and at least 30 % was located at sites with a high structural disorder similar to Sr<sup>2</sup>+ in solution. The remaining strontium was absorbed in collagen. The relative distribution of strontium among the different composites seemed to be independent of treatment period and dose level.</p>