Application of aluminum diffusion coatings to mitigate the KCl-induced high-temperature corrosion

Publication: Research - peer-reviewJournal article – Annual report year: 2016

DOI

View graph of relations

Pack cementation was used to produce Fe1−xAl and Fe2Al5 diffusion coatings on ferritic-martensitic steel P91 and a Ni2Al3 diffusion coating on pure nickel. The performance of diffusion coatings against high-temperature corrosion induced by potassium chloride (KCl) was evaluated by exposing the samples at 600 °C for 168 h in static lab air under KCl deposit. In addition, a salt-free experiment was performed for comparison. Microstructure, chemical and phase composition of the samples were analyzed with scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS) and X-ray diffractometry (XRD) before and after the exposures. It was found that all the diffusion coatings formed protective oxides under salt-free exposure in air. Under the salt deposit, Fe1−xAl showed local failure while on large parts of the sample a protective layer had formed. Fe2Al5 was attacked over the entire surface and the dominant mode of attack was selective aluminum removal. Ni2Al3 showed excellent performance and no sign of attack was observed anywhere on the sample.
Original languageEnglish
JournalMaterials and Corrosion
Volume68
Issue number1
Pages (from-to)82–94
Number of pages13
ISSN0947-5117
DOIs
StatePublished - 2017
CitationsWeb of Science® Times Cited: 0
Download as:
Download as PDF
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
Word

ID: 125834752