Analysis of the decomposition gases from α and β-Cd(BH4)2 synthesized by temperature controlled mechanical milling

Publication: Research - peer-reviewJournal article – Annual report year: 2012

View graph of relations

We present a comprehensive study on the controlled phase synthesis and thermal decomposition of Cd(BH2)4, a material for solid state hydrogen storage obtained via the metathesis reaction of LiBH4 with CdCl2. By adjusting the stochiometry of the reactants and controlling the mechanical milling vial temperature, we have isolated the tetragonal (P42mn) low temperature phase and the cubic (View the MathML source) high temperature phase of the cadmium borohydride. Cd(BH2)4 has a low thermodynamic stability and decomposes with fast kinetic at 348 K, when heated at 1 K min−1 against a backpressure of 1 bar H2. A semi-quantitative analysis reveals that the decomposition gases are composed of 1:1 H2 + B2H6 and that only Cd remains as solid crystalline phase.
Original languageEnglish
JournalJournal of Alloys and Compounds
Volume547
Pages (from-to)76-80
ISSN0925-8388
DOIs
StatePublished - 2013
Peer-reviewedYes
CitationsWeb of Science® Times Cited: 3

Keywords

  • Energy storage materials, Metal hydride, Mechanochemical processing, Diborane
Download as:
Download as PDF
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
Word

Download statistics

No data available

ID: 12735628